我們利用含浸塗佈加工的方式將水性PU塗佈在聚酯(PET)織物上，目的在將PET織物表面呈現更疏水的性質。塗佈加工過程是首先將水性聚胺酯(PU)預聚物與脂肪族撥水官能基一定比例合不同方式進行合成分散於水溶液中，並稀釋15％至5％含浸塗佈在PET織物上之後，其具有撥水官能基的水性PU分散液會在織品表面上，利用常溫硬化反應，形成化學鍵結的互穿式網狀交聯(IPN)系統，崁入織物纖維之間，其高度架橋水性PU樹脂使其固定在織物纖維間，進而提高其耐水洗性。常溫交聯型PU在最適加工條件下，經撥水加工後的織物其對水的接觸角超過135°，且經過50次洗滌後仍能維持其原有的撥水效果。

Polyurethane (PU) skeleton consists of hydrophobic side-chains has been known for textile water-repellency treatment. PU prepolymers with hydrophobic hydrocarbon side chains obtained from the reaction of Isophorone diisocyanate(IPDI), glycerol, a higher alcohol (e.g. cetyl alcohol), dimethylolpropanic acid (DMPA) and polytetramethylene glycol-2000 (PTMEG-2000) in various ratios. Self-curable aqueous-based PU system is prepared from these resulted PU prepolymers by conventional process with a multi-aziridine curing agent (TMPTA-AZ). The water repellent polyethylene terephthalate (PET) textile is obtained by the treatment of this aqueous PU system with various hydrocarbon side-chain contents by dipping process. Aqueous PU is self-cured on drying and its curing reaction resulted in the formation of highly cross-linked interpenetrating network (IPN). This cross-linked PU with hydrophobic side-chains anchored into fabric fibers that enhance the water washing durability of treated textiles. This treated water-repellent textile (PET) has a water contact angle over 135°only with PU containing long chain hydrocarbons side-chains without any content of 
fluorine or polysiloxane.

總     目     錄

中摘. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 

英摘. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 

誌謝. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 

一、序論. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 1
1-1 前言. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .1
1-2 織物撥水加工的說明. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .1
1-3 織物的撥水性. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .2
1-4新世紀消費者對撥水性織物. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4
1-5揮發性有機成分. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . ..5
1-6 研究動機與目的. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .5

二、文獻回顧. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .7
2-1 聚胺酯簡介. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .7
    2-1-1聚胺酯發展歷程. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .8
    2-1-2聚胺酯的基本材料. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .8
2-2 水性聚胺酯介紹. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .17
2-2-1 水性聚胺酯類型. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .18
2-2-2 水性PU分散液製造技術. . . . . . . . . . . . . . . . . . . . . . . . . . . .22
2-3 次乙亞胺之介紹. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .28
2-4 疏水性之介紹. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .33
2-5 表面能之簡介. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .35
    2-5-1 界面張力與表面張力之簡介. . . . . . . . . . . . . . . . . . . . . . . .36
    2-5-2 撥水理論. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .37
2-6 聚對苯二甲酸乙酯纖維. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .39
2-7 荷葉效應. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .40

三、實驗. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 43
3-1儀器. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 43
3-2化學藥品. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 44
3-3常溫架橋型水性聚胺酯合成步驟. . . . . . . . . . . . . . . . . . . . . . . . . . 46
3-3-1 DMPA-PTMEG-2000 Cetyl Prepolymer (末端型)之合成….46
3-3-2 DMPA-PTMEG-2000 Cetyl WPU分散液(末端型)之合成…47
    3-3-3 IPDI-Glycerol Oligomer合成. . . . . . . . .. . . . . . . . . . . . . . . . 48
    3-3-4 IPDI-Glycerol-Cetyl Alcohol Oligomer之合成. . . . . . . . . . .49
    3-3-5 DMPA-PTMEG-2000-Cetyl Alcohol WPU分散液之合成...50
    3-3-6 DMPA-PTMEG-2000 Prepolymer之合成. . . . . . . . . . . . . . .52
    3-3-7 Cetyl oligomer ／ WPU分散液之合成 . . . . . . . . . . . . . . .53
3-4 常溫架橋型織物撥水加工. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .55
  3-4-1 PTMEG-DMPA-Cetyl Alcohol WPU分散液織物撥水加工55
3-4-2 PTMEG-DMPA-Stearic Acid WPU分散液織物撥水加工..57
3-5 固含量測試 (Solid Content) . . . . . . . . . . . . . . . . . . . . . . . . . . . . .58
3-6 聚胺酯預聚物異氰酸酯含量(NCO %)測定. . . . . . . . . . . . . . . . .58
3-7紅外線光譜(FT-IR)鑑定. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .60
3-8織物表面之靜態接觸角(Static Contact Angle)測定. . . . . . . . . . . . .60
3-9織物表面之滑動角(Sliding Angle)測定. . . . . . . . . . . . . . . . . . . . .61
3-10 織物水洗堅牢度測試(AATCC-135-2004) . . . . . . . . . . . . . . . . . .62
    3-10-1洗滌流程. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .62
    3-10-2洗滌操作條件. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .63

四、結果與討論. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 64
4-1常溫架橋型水性聚胺酯合成之織物撥水加工應用. . . . . . . . . . . . 64
4-2常溫架橋型織物撥水效果探討. . . . . . . . . . . . . . . . . . . . . . . . . . . . 65
    4-2-1含脂肪族撥水官能基水性聚胺酯末端型. . . . . . . . . . . . . . .65
    4-2-2含脂肪族撥水官能基水性聚胺酯嵌段型. . . . . . . . . . . .66
    4-2-3含脂肪族撥水劑與水性聚胺酯後固化型. . . . . . . . . . . . . . .67
    4-2-4含脂肪族撥水官能基水性聚胺酯側鏈型. . . . . . . . . . . . . . 68
4-2-4A含脂肪族撥水官能基水性聚胺酯側鏈型塗佈率探討
 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .70
4-2-4B含脂肪族撥水官能基水性聚胺酯側鏈型架橋劑濃度
探討. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 74
4-2-4C含脂肪族撥水官能基水性聚胺酯側鏈型耐水洗效果
探討. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 78
    4-2-5含脂肪族撥水官能基水性聚胺酯側鏈部分交聯型. . . . . . .85
4-2-5A含脂肪族撥水官能基水性聚胺酯側鏈部分交聯型物
理性質探討. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 85
4-2-5B含脂肪族撥水官能基水性聚胺酯側鏈部分交聯型耐
水洗能力探討. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 86
4-2-5C含脂肪族撥水官能基水性聚胺酯側鏈部分交聯型架
橋劑濃度探討. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 96

五、結論. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 99

六、參考文獻. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .101
圖   表   目   錄

Scheme 1. DMPA-PTMEG-2000 Cetyl Prepolymer (末端型)之合成. . 46
Scheme 2. DMPA-PTMEG-2000 Cetyl WPU分散液(末端型)之合成. 47
Scheme 3. IPDI-Glycerol Oligomer 之合成. . . . . . . . . . . . . . . . . . . . . 48
Scheme 4. IPDI-Glycerol Oligomer 之合成. . . . . . . . . . . . . . . . . . .49
Scheme 5. DMPA-PTMEG-2000-Cetyl Alcohol Prepolymer之合成. . .51
Scheme 6 DMPA-PTMEG-2000 Prepolymer 之合成. . . . . . . . . . . . . . 52
Scheme 7 DMPA-PTMEG-2000-Cetyl Alcohol WPU分散液之合成. . 54
Scheme 8 DMPA-PTMEG-2000 Cetyl Alcohol WPU含浸示意圖. . . . 55
Scheme 9 DMPA-PTMEG-2000 Cetyl WPU(末端)含浸示意圖. . . . . . 56
Scheme10 Stearic Acid & DMPA-PTMEG-2000 WPU含浸示意圖. . . 57















表2-5-1 表面結構所具有的官能基之表面張力. . . . . . . . . . . . . . . . . 36
表3-10-2a 洗滌和乾燥程序. . . . . . . . . . . . . . . . . . . . . . . . . . . 63
表3-10-2b 洗衣機條件. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 63
表3-10-2c 乾衣機條件. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .63
表4-1 Contact Angle of B-Cetyl-WPU 17.2. . . . . . . . . . . . . . . . . . . . . .66
表4-2 Physical Properties of ST-WPU 17.3(15%) . . . . . . . . . . . . . . . . . 67
表4-3 Contact Angles of S-Cetyl-WPU 19.3. . . . . . . . . . . . . . . . . . . . . .69
表4-4 Contact Angles of S-Cetyl-WPU 18.6. . . . . . . . . . . . . . . . . . . . . .69
表4-5-1 S-Cetyl-WPU 18.6 Contact Angle to TMPTA-AZ . . . . . . .71
表4-5-2 S-Cetyl-WPU 18.6 Sliding Angle to TMPTA-AZ. . . . . . . . . .72
表4-6-1 S-Cetyl-WPU 18.6 Physical Properties to TMPTA-AZ(5%) . . 75
表4-6-2 S-Cetyl-WPU 18.6 Physical Properties to TMPTA-AZ(10%). .76
表4-6-2 S-Cetyl-WPU 18.6 Physical Properties to TMPTA-AZ(15%) 77
表4-7-1 S-Cetyl-WPU 18.6 Washing Durability to TMPTA-AZ(0.75N)80
表4-7-2 S-Cetyl-WPU 18.6 Washing Durability to TMPTA-AZ(1.5N) .82
表4-7-3 S-Cetyl-WPU 18.6 Washing Durability to TMPTA-AZ (3.0N).83
表4-8-1 Physical properties of S-Cetyl-WPU 13.9 (TMPTA-AZ 0N). .88
表4-8-2 Physical properties of S-Cetyl-WPU 13.9 (TMPTA-AZ 0.5N).90
表4-8-3 Physical properties of S-Cetyl-WPU 13.9 (TMPTA-AZ 1.0N).92
表4-8-4 Physical properties of S-Cetyl-WPU 13.9 (TMPTA-AZ 2.0N) 94
表4-8-5 SP-Cetyl-WPU 13.9 Physical Properties to TMPTA-AZ(15%)
 After 50th Washing Cycles. . . . . . . . . . . . . . . . . . . . . . . . . . . . .96

































圖2-1 羧酸鹽和磺酸鹽型乳化劑. . . . . . . . . . . . . . . . . . . . . . . . . . . .18
圖2-2  陰離子型水性聚胺酯分散液. . . . . . . . . . . . . . . . . . . . . . . . . 19
圖2-3  陽離子型水性聚胺酯分散液. . . . . . . . . . . . . . . . . . . . . . . . . 20
圖2-4  非離子型水性PU分散液. . . . . . . . . . . . . . . . . . . . . . . . . . . 21
圖2-5  丙酮加工法流程圖. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 23
圖2-6  預聚物離子混合加工法流程圖 . . . . . . . . . . . . . . . . . . . . . .24
圖2-7  熱融加工法流程圖 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .25
圖2-8  酮亞胺/酮連氮加工法流程圖 . . . . . . . . . . . . . . . . . . . . . . . . .27
圖2-3-1 Aziridine質子化 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 29
圖2-3-2 Aziridine自身聚合示意圖 . . . . . . . . . . . . . . . . . . . . . . . . . . . 30
圖2-3-3 Aziridine鏈延長示意圖. . . . . . . . . . . . . . . . . . . . . . . . . . . 30
圖2-3-4 PEI基本架構 . . . . . . . . . . . . . . . . . . . . . . . . . . . .31
圖2-3-5 Linear Polyethyleneimine . . . . . . . . . . . . . . . . . . . . . . . . . . 32
圖2-5-1 液體滴落固體表面的接觸角大小 . . . . . . . . . . . . . . . . . . . . 37
圖2-6-1 聚對苯二甲酸乙酯化學結構. . . . . . . . . . . . . . . . . . . . . . . . . 39
圖2-7-1 荷葉表面上的污物被水帶走的實際微觀情形 . . . . . . . . . . 42
圖3-8-1 接觸角測試示意圖 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .61
圖3-9-1 測量水滴滑動角的滑動情形 . . . . . . . . . . . . . . . . . . . . . . . . 61
圖4-1a S-Cetyl-WPU 18.6 Contact Angle to Coating Raito (0.75N) . . .71
圖4-1b S-Cetyl-WPU 18.6 Contact Angle to Coating Raito (1.5N) . . . .71
圖4-1c S-Cetyl-WPU 18.6 Contact Angle to Coating Raito (3.0N). . . . 72
圖4-2a S-Cetyl-WPU 18.6 Sliding Angle to Coating Raito (0.75N) . . . 72
圖4-2b S-Cetyl-WPU 18.6 Sliding Angle to Coating Raito (1.5N) . . . . 73
圖4-2c S-Cetyl-WPU 18.6 Sliding Angle to Coating Raito (3.0N) . . . . 73
圖4-3a Contact Angle of S-Cetyl-WPU 18.6 (5%) . . . . . . . . . . . . . . . . .75
圖4-3b Sliding Angle of S-Cetyl-WPU 18.6 (5%). . . . . . . . . . . . . . . . . 75
圖4-4a Contact Angle of S-Cetyl-WPU 18.6 (10%) . . . . . . . . . . . . . . . .76
圖4-4b Sliding Angle of S-Cetyl-WPU 18.6 (10%) . . . . . . . . . . . . . . . .76
圖4-5a Contact Angle of S-Cetyl-WPU 18.6 (15%). . . . . . . . . . . . . . . . 77
圖4-5b Sliding Angle of S-Cetyl-WPU 18.6 (15%). . . . . . . . . . . . . . . . 77
圖4-6a S-Cetyl-WPU 18.6 Washing Durability 0.75N (Coating Ratio) .81
圖4-6b S-Cetyl-WPU 18.6 Washing Durability 0.75N (Wetting Time) .81
圖4-7a S-Cetyl-WPU 18.6 Washing Durability 1.5N (Coating Ratio) . .82
圖4-7b S-Cetyl-WPU 18.6 Washing Durability 1.5N (Wetting Time) . .83
圖4-8a S-Cetyl-WPU 18.6 Washing Durability 3.0N (Coating Ratio) . .84
圖4-8b S-Cetyl-WPU 18.6 Washing Durability 3.0N (Wetting time) . . 84
圖4-9-1a Contact Angles of SP-Cetyl-WPU 13.9 (0N) . . . . . . . . . . . . . 88
圖4-9-1b Sliding Angles of SP-Cetyl-WPU 13.9 (0N) . . . . . . . . . . . . . 89
圖4-9-1c Wetting Time of SP-Cetyl-WPU 13.9 (0N). . . . . . . . . . . . . . . 89
圖4-9-2a Contact Angles of SP-Cetyl-WPU 13.9 (0N). . . . . . . . . . . . . .90
圖4-9-2b Wetting Time of SP-Cetyl-WPU 13.9 (0.5N) . . . . . . . . . . . . . 91
圖4-9-2c Sliding Angles of SP-Cetyl-WPU 13.9 (0.5N). . . . . . . . . . . . .91
圖4-9-3a Contact Angles of SP-Cetyl-WPU 13.9 (1.0N). . . . . . . . . . . 92
圖4-9-3b Sliding Angles of SP-Cetyl-WPU 13.9 (1.0N). . . . . . . . . . . . .93
圖4-9-3c Wetting Time of SP-Cetyl-WPU 13.9 (1.0N) . . . . . . . . . . . . . 93
圖4-9-4a Contact Angles of SP-Cetyl-WPU 13.9 (2.0N) . . . . . . . . . . . .94
圖4-9-4b Sliding Angles of SP-Cetyl-WPU 13.9 (2.0N) . . . . . . . . . . . . 95
圖4-9-4c Wetting Time of SP-Cetyl-WPU 13.9 (2.0N). . . . . . . . . . . . . .95
圖4-9-5a Contact Angle of SP-Cetyl-WPU 13.9 (15%). . . . . . . . . . . . . 97
圖4-9-5b Sliding Angle of SP-Cetyl-WPU 13.9 (15%). . . . . . . . . . . . . .97
圖4-9-5c Wetting Time of SP-Cetyl-WPU 13.9 (15%) . . . . . . . . . . . . . .98

1.　中興紡織公司, 超耐久撥水性織物-Hinamo, 織布會刊, 2001, Vol. 
29期.
2.  An Introduction to Indoor Air Quality, US EPA website
3.　F. C. Chang, 2003, Chapter 18, 437.
4.　G. N. Chen, K. N. Chen, Journal of Applied Polymer Science, 1999, 
71, 903.
5.　J. Casado, V. Hernandez, Journal of the American Chemical Society, 
2005, 127, 13364.
6.　H. J. Ling, G. N. Chen, K. N. Chen, Advanced Engineering   
   Materials, 1999, 2, 114.
7.　黃景忠, 紫外光硬化型PU/二氧化矽奈米複合材料於表面塗裝之
應用, 淡江大學化學系碩士論文, 2007
8.　J. W. Rosthauser and K. Nachtakamp J. Coating Fabrics 1986, 16, 
　 39.
9.　D. Dieterich, Prog. Org. Coatings 1981, 9, 281.
10. D. Dieterich, Polyurethane Handbook, New York, 1985, Chapter2
11. A. A. Wolfrey 1981, U. S. Patent 4,278,578
12. G. R. Wactchko 1981, U. S. Patent 4,301,053
13. C. D. Dudgeon and M. R. Winstead 1985, U. S. Patent 4,493,912
14. A. Noshay and J. E. McGrath Block Copolymers 1977, 364.
15. D. E. Hudgin, Handbook of Polymer Synthesis, 1992
16. S. Y. Lee, J. S. Lee ,and B. K. Kim Polym. Int. 1997, 42, 67.
17. A. K. Nanda, D. A. Wicks, S. A. Madbouly, and J. U. Otaigbe J. Appl. Polym. Sci. 2005, 98,2514.
18. J. Z. Lai, H. J. Ling, J. T. Yeh and K. N. Chen J. Appl. Polym. Sci. 
2004, 91, 1997.
19. J. Z. Lai, J. T. Yeh and K. N. Chen J. Appl. Polym. Sci. 2005, 97, 550.
20. Z.S.Petrovic and J.Ferguson, Prog. Polym. Sci 1991, 16, 695.
21. 賴建志 淡江大學化學學系博士班論文, 2004
22. 黃清澤 淡江大學化學學系博士班論文, 2005
23. 張豐志 應用高分子手冊, 五南出版社, 2003
24. 顏明雄、張昌榮 化工技術, 2005, 13, 167
25. 徐武軍 高分子材料導論, 五南出版社, 2004
26. 葉明國 聚合物化學, 新學識文教出版中心, 2001
27. 張惠郁 2001年全球環氧樹脂市場概況, 工研院
28. H. Wenker, Journal of American Chemical Society, 57, 2328 (1935)
29. J.W. Rosthauser, K. Nachtakamp, Journal of Coated Fabrics, 16, 39 
(1986)
30. D. Dieterich, Progress in Organic Coatings, 9, 281 (1981)
31. C.H. Shao, T.Z. Wang, G.N. Chen, K.J. Chen, J.T. Yeh, K.N. 
　 Chen, Journal of Polymer Research, 7, 41 (2000)
32. K. Geckeler, G. Lange, H. Eberhardt, E. Bayer, Pure and Applied 
Chemistry, 52, l88 (1980)
33. C.D. Dudgeon, M.R. Winstead, U. S. Patent, 4, 493, 912 (1985)
34. E.G. Shur, Americal Paint Journal, Sep. 4 (1972)
35. L. Kanerva, H. Keskinen, P. Autio, Clinical and Experimental Allergy, 
25, 432 (1995)
36. E.J. Goethals, R.R. Declercq, New Method for Polymer Synthesis, 
Chap 3 (1992)
37. P.-C. Chen, S.-C. Wang, C.-Y. Huang, J.-T. Yeh, K.-N. Chen, Journal 
of Applied Polymer Science, 104, 809 (2006)
38. 陳威宏, 高分子材料應用在功能化塗裝之研究開發, 淡江大學化
    學系博士論文, 2009.
39. 林析右, 固著液滴表面張力與接觸角之新測量技術, 臺灣工業技
    術學院化學工程技術系, 1995.
40. J. Bico, U. Thiele, D. Quere, Colloids and Surfaces A:
Physicochemical and Engineering Aspects, 2002, 206, 41.
41. R. N. Wenzel, Industrial and Engineering Chemistry, 1936, 28.
42.	A.B.D. Cassie, S. Baxter, Transactions of the Faraday Society, 1944, 
   40, 546.
43. 陳威狀, 自行架橋型高分子於阻然/撥水的製備與研究應用, 淡江
   大學化學系碩士論文, 2008.
44. W. Wu, Q. Zhu, F. Qing, C. C. Han, Langmuir, 2008, 25, 17.
45. J. Stephen, J. Clarson, A. Semlyen, Siloxane Polymers, 1993.
46. 吳至德, 尼龍表面親疏水性之研究, 中央大學化學工程與材
   料工程學系碩士論文, 2005.
47. 卡特, 纖維化學, 1980.
48. W. Barthlott, C. Neinhuis, Planta, 1997, 202, 1.